ISL Petrolatum Tape HT 50mm x 10m (High Temperature) ISL Petrolatum Tape High Temperature is composed of a non-woven synthetic fabric carrier, fully impregnated with a neutral petrolatum compound, stabilised with inert fillers and complemented with corrosion inhibitors. For operating temperatures up to 75°C. ISL Petrolatum Tape HT is deigned to provide long term corrosion protection to pipes, flanges, valves, and other fittings. Features

• Surface Tolerance on marginally prepared substrates; St 2.0.

• Conforms to irregular shapes and profiles.

• Can be applied to cold, wet substrates.

• Unaffected by water, acid, salts, or bacterial attack.

• Encapsulates lead painted substrates.

• Nil VOC's.

• Ease of application at high and low temperature extremes.

• Ready for immediate service, no curing time.

• Conforms with AWWA C 217-04. Application

• Prepare surface to St 2 std.

• Apply ISL Petrolatum Primer to substrate at a spread rate of 3kg/m² approx.

• Profile projections and voids with ISL Petrolatum Mastic.

• Spirally apply tape incorporating 55% overlap to achieve a double thickness with circumferential turn.

• Overwrap tape with UCC PVC OverWrap, spirally applied with 55% overlap. Product Properties: Properties | Test Method | Value

• Thickness | ASTM D1000 | 1.1mm to 1.5mm

• Weight | 1.44kg/m² | 1.44kg/m²

• Breaking Strength | ASTM D1000 | 6.0 N/mm

• Elongation at Break | ASTM D1000 | 15%

• Breakdown Voltage (2 layers) | ASTM D149 | >16kv

• Water Vapour Transmission Rate | ASTM E96 | 0.25g/m² /24hr

• Cathodic Disbondment | ASTM G8 | <700mm² Application Temperature: -10 to +55ºC Service Temperature: -20 to +75ºC Excursion Peak Temperature: 80ºC Manufactured by; UNIVERSAL CORROSION COATINGS PTY LTD, VICTORIA

ISL Petrolatum Tape HT 50mm x 10m (High Temperature) ISL Petrolatum Tape High Temperature is composed of a non-woven synthetic fabric carrier, fully impregnated with a neutral petrolatum compound, stabilised with inert fillers and complemented with corrosion inhibitors. For operating temperatures up to 75°C. ISL Petrolatum Tape HT is deigned to provide long term corrosion protection to pipes, flanges, valves, and other fittings. Features

• Surface Tolerance on marginally prepared substrates; St 2.0.

• Conforms to irregular shapes and profiles.

• Can be applied to cold, wet substrates.

• Unaffected by water, acid, salts, or bacterial attack.

• Encapsulates lead painted substrates.

• Nil VOC's.

• Ease of application at high and low temperature extremes.

• Ready for immediate service, no curing time.

• Conforms with AWWA C 217-04. Application

• Prepare surface to St 2 std.

• Apply ISL Petrolatum Primer to substrate at a spread rate of 3kg/m² approx.

• Profile projections and voids with ISL Petrolatum Mastic.

• Spirally apply tape incorporating 55% overlap to achieve a double thickness with circumferential turn.

• Overwrap tape with UCC PVC OverWrap, spirally applied with 55% overlap. Product Properties: Properties | Test Method | Value

• Thickness | ASTM D1000 | 1.1mm to 1.5mm

• Weight | 1.44kg/m² | 1.44kg/m²

• Breaking Strength | ASTM D1000 | 6.0 N/mm

• Elongation at Break | ASTM D1000 | 15%

• Breakdown Voltage (2 layers) | ASTM D149 | >16kv

• Water Vapour Transmission Rate | ASTM E96 | 0.25g/m² /24hr

• Cathodic Disbondment | ASTM G8 | <700mm² Application Temperature: -10 to +55ºC Service Temperature: -20 to +75ºC Excursion Peak Temperature: 80ºC Manufactured by; UNIVERSAL CORROSION COATINGS PTY LTD, VICTORIA